Molecular sieve has clear pore cavity distribution, extremely high internal surface area (600m2/s), good thermal stability (1000 ℃), and adjustable acid site center. The acidity of molecular sieve mainly comes from three coordinated aluminum atoms and aluminum ions (AlO)+on the framework and in the pores. OH based acid sensitive site center on molecular sieve HY obtained by ion exchange, Special activated carbon for catalyst carrier Ji'an The aluminum ions outside the framework will strengthen the acid site and form the L acid site center. Polyvalent cations such as Ca2+, Mg2+and La3+can show the acid site center after exchange. The reduction of transition metal ions such as Cu2+and Ag+can also form acid site centers. In general, the higher the Al/Si ratio, the higher the specific activity of OH group. The modification of zeolite acidity can introduce protons through direct exchange of dilute hydrochloric acid. This method often leads to dealumination of molecular sieve framework. So NaY will become NH4Y and then HY. Because there are uniform small internal pores in the structure of molecular sieves, when the molecular linearity of reactants and products is close to the pore size in the crystal, the selectivity of catalytic reaction often depends on the corresponding size of molecules and pore size. Special activated carbon for catalyst carrier high quality This selectivity is called shape selective catalysis. There are two mechanisms leading to shape selectivity. One is caused by the difference of diffusion coefficient of molecules participating in the reaction in the pore cavity, which is called mass transfer selectivity; The other is caused by the space limitation of the transition state of the catalytic reaction, which is called transition state selectivity.

Special activated carbon for catalyst carrier high quality Microporous molecular sieves with molecular apertures below 2 nm, mesoporous molecular sieves with molecular apertures above 50 nm (macroporous molecular sieves with molecular apertures above 50 nm), mesoporous molecular sieves have high specific surface area, regular and orderly pore structure, narrow pore size distribution, continuous and adjustable pore size and other characteristics, which make it difficult to complete the adsorption and separation of macromolecules in many microporous molecular sieves, And catalytic reaction. Therefore, molecular sieve materials with different properties and pore sizes shall be configured according to the different components of organic waste gas during selection, so as to achieve targeted organic waste gas treatment, meet the design requirements and emission standards. The main material of honeycomb zeolite adsorbent is natural zeolite. The manufacturer of zeolite is composed of silica Inorganic microporous material composed of al_2o_3 and alkaline metal or alkaline earth metal, with inner pore volume accounting for 40-50% of the total volume and specific surface area of 100-500 m2/g, has the characteristics of high temperature resistance, non flammability, good thermal stability and hydrothermal stability. It is an efficient molecular sieve carrier with good adsorption performance, no secondary pollution, and high temperature regeneration. Compared with honeycomb activated carbon, its performance is about 25% of its efficiency Special activated carbon for catalyst carrier Ji'an However, it is widely used in the fields of adsorption, separation, catalysis and environment due to its high temperature resistance and low ignition resistance. It is more suitable for the treatment of organic waste gas with large air volume and low concentration.

Ji'an Special activated carbon for catalyst carrier Zeolite is a porous aluminosilicate crystal (a1uminsi1ict) with a water bearing frame structure, which exists naturally in nature and is also artificially synthesized. The ideal chemical formula of zeolite can be expressed as Mx/yA1XSiyO2 (x y) P? H2O, In the formula, M refers to alkali metals (such as Na, K, Li) and alkaline earth metals (such as Ca, Mg, Ba, Sr). The chemical composition of zeolite is generally considered to be composed of A12O3, SiO2, H2O and metal cations, of which A12O3 and SiO2 account for about 80% of the total amount of zeolite minerals. In different zeolite minerals, the proportion of silicon and aluminum is different, Special activated carbon for catalyst carrier manufactor And the different proportion of zeolite will cause some changes in zeolite characteristics, such as ion exchange and acid resistance. Because the silicon (aluminum) oxygen tetrahedron of natural zeolite crystal has many holes and channels, which occupy cations and water molecules. When some other goods are completely dehydrated after baking, the crystal skeleton is not damaged, but forms large holes on the inner surface, which can absorb and store a large number of molecules, so it has the characteristics of large adsorption capacity and high selectivity.

Special activated carbon for catalyst carrier high quality 1. From the composition of both, carbon molecular sieve is an excellent non-polar carbon material, while zeolite molecular sieve is a hydrate of crystalline aluminosilicate metal salt. The two are completely different in the periodic table of chemical elements! 2. With different pore sizes, the pore composition of zeolite molecular sieves is obviously registered, which can be generally divided into macropores, mesopores and micropores, and there are interconnections between the pores, while carbon molecular sieves are generally micropores! 3. The adsorption principle is different. Zeolite molecular sieves absorb molecules of certain size and repel molecules of larger substances. Special activated carbon for catalyst carrier Ji'an Carbon molecular sieve contains a large number of micropores, which can effectively separate the components of gas mixture. 4. The uses are also different. Carbon molecular sieves are widely used in coal fields, petroleum, chemicals, metal heat treatment, electronic manufacturing, food preservation and other industries, while zeolite molecular sieves can be used in addition to petroleum, chemicals, natural gas, electronic production, industrial gas separation, pharmaceutical industry, refrigeration industry, and hollow glass manufacturing.