Small block activated carbon Hubei Because the aluminum oxide tetrahedron of zeolite has a negative charge, and the skeleton hole contains cations, a strong electric field is formed around the cations. Therefore, the adsorption force of zeolite not only has a strong dispersion force, but also has a large electrostatic force. It is precisely because of this electrostatic relationship that zeolites have preferential selective adsorption on polar, unsaturated and polarizable molecules. It can strongly adsorb molecules containing polar groups such as hydroxyl ion, ammonium ion and other polarizable groups, especially water, which can form hydrogen bonds with aluminum silicon skeleton, so zeolite has strong water absorption. It can still adsorb even under low relative humidity and concentration, and its water absorption is higher than that of silica gel and activated alumina. The main material of honeycomb zeolite adsorbent is natural zeolite. The manufacturer of zeolite is composed of silica Inorganic microporous material composed of al_2o_3 and alkaline metal or alkaline earth metal, with inner pore volume accounting for 40-50% of the total volume and specific surface area of 100-500 m2/g, is characterized by high temperature resistance, non flammability, good thermal stability and hydrothermal stability. It is an efficient molecular sieve carrier with good adsorption performance, no secondary pollution, and can be regenerated at high temperature. Compared with honeycomb activated carbon, its performance is about 25% of its efficiency, However, it is widely used in the fields of adsorption, separation, catalysis and environment due to its high temperature resistance and difficult ignition. It is more suitable for the treatment of organic waste gas with large air volume and low concentration.

Honeycomb zeolite molecular sieve is an efficient molecular sieve carrier with good adsorption performance, no secondary pollution and high temperature regeneration. It is widely used in the fields of adsorption, separation, catalysis and environment, Small block activated carbon major It is more suitable for the treatment of organic waste gas with large air volume and low concentration. It is widely used in the production of basic organic chemical industry and petrochemical industry, as well as in the treatment of harmful gases, SO2 NOx、CO、CO2，NH3，CCl4、 Purification of water vapor and gaseous hydrocarbon waste gas. Strong adsorption selectivity: molecular sieve materials with different properties and pore sizes are configured for the product according to the different components of organic waste gas, so as to achieve targeted and selective treatment of organic waste gas, meet the design requirements and meet the emission standards. 2. Strong adsorption capacity: even if the gas composition concentration is very low at the mg level, it still has the adsorption capacity. The efficiency is 50% higher than that of similar activated carbon. 3. Wide adaptability of adsorption temperature: at a higher temperature, it still has a large adsorption capacity, while other adsorbents are greatly affected by temperature, so under the same temperature, the adsorption capacity of molecular sieve is large. 4. Good regeneration temperature resistance: the concentration ratio of pollutants after adsorption and concentration by molecular sieve can reach 15 to 20 times, and the concentrated waste gas can be condensed and recovered or burned at high temperature as required 5. High strength: Small block activated carbon Direct selling Products coming to the company use special framework materials to make the positive pressure strength of honeycomb zeolite reach more than 3Mpa, which can reduce damage during transportation and installation.

Molecular sieve is a crystalline silicate or aluminosilicate, which is a pore and cavity system with molecular size (usually 0.3nm to 2.0nm) formed by connecting silicon oxygen tetrahedron or aluminum oxide tetrahedron through oxygen bridge bond, Small block activated carbon Hubei Therefore, it has the characteristics of screening molecules. However, with the deepening of molecular sieve synthesis and application research, researchers have found phosphoaluminate molecular sieves, and the skeleton elements (silicon or aluminum or phosphorus) of molecular sieves can also be replaced by B, Ga, Fe, Cr, Ge, Ti, V, Mn, Co, Zn, Be and Cu, and the size of its pores and cavities can also reach more than 2 nm, Small block activated carbon major Therefore, molecular sieves can be divided into silicon aluminum molecular sieves, phosphorus aluminum molecular sieves and skeleton heteroatom molecular sieves according to the composition of skeleton elements;

Small block activated carbon major The evaluation of the adsorption of zeolite depends not only on whether the specific surface area of zeolite is large enough, but also on whether the equipment is hydrophobic. When purchasing, people can choose the inspection equipment. When the air humidity for the hydrophobicity of the inspection equipment is greater than 60%, if the equipment is blocked and the machine works abnormally, people should carefully consider whether to purchase the equipment. It is important to know that the adsorption and hydrophobicity of the zeolite runner are equally important. The zeolite content of the zeolite runner is proportional to the adsorption concentration efficiency. Therefore, many people should pay more attention to whether the zeolite content of the equipment meets the requirements or is high enough when choosing to purchase the zeolite runner. On the one hand, selecting excellent equipment is also to enhance the potential value of the enterprise. Small block activated carbon Hubei The adsorption and concentration technology of zeolite runner is deeply loved by enterprises because of its high efficiency and energy saving characteristics. Its changeable working environment and low cost have laid an unshakable position for zeolite runner in industry. How to select a zeolite runner with stable operation and high efficiency needs people's eyes