Activated Carbon Jiujiang Because the aluminum oxide tetrahedron of zeolite has a negative charge, and the skeleton hole contains cations, a strong electric field is formed around the cations. Therefore, the adsorption force of zeolite not only has a strong dispersion force, but also has a large electrostatic force. It is precisely because of this electrostatic relationship that zeolites have preferential selective adsorption on polar, unsaturated and polarizable molecules. It can strongly adsorb molecules containing polar groups such as hydroxyl ion, ammonium ion and other polarizable groups, especially water, which can form hydrogen bonds with aluminum silicon skeleton, so zeolite has strong water absorption. It can still adsorb even under low relative humidity and concentration, and its water absorption is higher than that of silica gel and activated alumina. The main material of honeycomb zeolite adsorbent is natural zeolite. The manufacturer of zeolite is composed of silica Inorganic microporous material composed of al_2o_3 and alkaline metal or alkaline earth metal, with inner pore volume accounting for 40-50% of the total volume and specific surface area of 100-500 m2/g, is characterized by high temperature resistance, non flammability, good thermal stability and hydrothermal stability. It is an efficient molecular sieve carrier with good adsorption performance, no secondary pollution, and can be regenerated at high temperature. Compared with honeycomb activated carbon, its performance is about 25% of its efficiency, However, it is widely used in the fields of adsorption, separation, catalysis and environment due to its high temperature resistance and difficult ignition. It is more suitable for the treatment of organic waste gas with large air volume and low concentration.

Because there are uniform small internal pores in the molecular sieve structure, Activated Carbon Jiujiang When the molecular linear degree of reactants and products is close to the pore size of the crystal, the selectivity of catalytic reaction often depends on the corresponding size of the molecule and pore size. This selectivity is called shape selective catalysis. There are two mechanisms leading to shape selectivity. One is caused by the difference of diffusion coefficient of molecules participating in the reaction in the pore cavity, which is called mass transfer selectivity; The other is caused by the space limitation of the transition state of the catalytic reaction, which is called transition state selectivity. Molecular sieve has clear pore cavity distribution, extremely high internal surface area (600m2/s), good thermal stability (1000 ℃), and adjustable acid site center. The acidity of molecular sieve mainly comes from three coordinated aluminum atoms and aluminum ions (AlO)+on the framework and in the pores. The OH based acid sensitive site center on the molecular sieve HY obtained by ion exchange, and the aluminum ion outside the framework will strengthen the acid site, forming the L acid site center. Polyvalent cations such as Ca2+, Mg2+and La3+can show the acid site center after exchange. The reduction of transition metal ions such as Cu2+and Ag+can also form acid site centers. In general, the higher the Al/Si ratio, the higher the specific activity of OH group. The modification of zeolite acidity can introduce protons through direct exchange of dilute hydrochloric acid. Activated Carbon high quality This method often leads to dealumination of molecular sieve framework. So NaY will become NH4Y and then HY.

The holes and channels inside the zeolite crystal are uniform and fixed in size, and the diameter of the holes is generally 6~15A. Activated Carbon Jiujiang Only molecules with smaller diameter can enter the cavity through the zeolite channel and be adsorbed, while large molecules cannot enter the cavity and be adsorbed. Zeolite is also called molecular sieve because of its selective adsorption performance. However, silica gel, activated carbon and other adsorbents have no selective adsorption and screening performance due to their non uniformly fixed pore sizes and large changes. Shunyi zeolite filter material price. Because the silicon (aluminum) oxygen tetrahedron of natural zeolite crystal has many holes and channels, which occupy cations and water molecules. When some other goods are completely dehydrated after baking, the crystal skeleton is not damaged, but forms large holes on the inner surface, which can absorb and store a large number of molecules, so it has the characteristics of large adsorption capacity and high selectivity. Activated Carbon high quality In different zeolite minerals, the proportion of silicon and aluminum is different, and the different proportion will cause some characteristics of zeolite changes, such as ion exchange and acid resistance.

Activated Carbon Jiujiang The adsorption and concentration technology of zeolite runner is highly praised by enterprises because of its high efficiency and energy saving. Its changeable working environment and low cost ensure the popularization and application of zeolite runner in industry. How to select a zeolite runner with stable operation and high efficiency? The zeolite content of the zeolite runner is proportional to the adsorption concentration efficiency. Therefore, when choosing to purchase the zeolite runner, the matching zeolite content should be selected in combination with the emission concentration of the enterprise's exhaust gas pollutants. Zeolites with large specific surface area shall be purchased for good hydrophobicity. Select the inspection equipment to test the hydrophobicity of the equipment. When the air humidity is greater than 60%, calibrate the equipment. If the equipment is blocked and the machine works abnormally, it indicates that the equipment has poor hydrophobicity, and you should carefully consider whether to purchase the equipment. The factors affecting the purification efficiency of zeolite due to high desorption efficiency are: absorption on the one hand and desorption function on the other. Activated Carbon high quality If the waste gas adsorbed on the runner cannot be completely desorbed, the runner will become saturated after a long time, which will affect the adsorption efficiency of the zeolite runner and directly affect the service life of the zeolite over time.