Jiujiang Activated Carbon Zeolite is a porous aluminosilicate crystal (a1uminsi1ict) with a water bearing frame structure, which exists naturally in nature and is also artificially synthesized. The ideal chemical formula of zeolite can be expressed as Mx/yA1XSiyO2 (x y) P? H2O, Where, M is alkali metal (such as Na, K, Li) and alkaline earth metal (such as Ca, Mg, Ba, Sr). The chemical composition of zeolite is generally considered to be composed of A12O3, SiO2, H2O and metal cations, of which A12O3 and SiO2 account for about 80% of the total zeolite minerals. In different zeolite minerals, the proportion of silicon and aluminum is different, Activated Carbon manufactor And the different proportion of zeolite will cause some changes in zeolite characteristics, such as ion exchange and acid resistance. Because the silicon (aluminum) oxygen tetrahedron of natural zeolite crystal has many holes and channels, which occupy cations and water molecules. When some other goods are completely dehydrated after baking, the crystal skeleton is not damaged, but forms large holes on the inner surface, which can absorb and store a large number of molecules, so it has the characteristics of large adsorption capacity and high selectivity.

Activated Carbon high quality Because the silicon (aluminum) oxygen tetrahedron of natural zeolite crystal has many holes and channels, which occupy cations and water molecules. When some other goods are completely dehydrated after baking, the crystal skeleton is not damaged, but forms large holes on the inner surface, which can absorb and store a large number of molecules, so it has the characteristics of large adsorption capacity and high selectivity. There are cavities and channels in the crystal structure of zeolite with large adsorption capacity, whose volume accounts for more than 50% of the total volume of zeolite crystals. Moreover, the micropores of zeolite are evenly distributed, and the pore size is small, which is equivalent to the molecular size of general substances. The internal surface area of zeolite crystals can reach more than 1000 square meters. Therefore, the adsorption capacity of zeolite is particularly large. Activated Carbon manufactor In different zeolite minerals, the proportion of silicon and aluminum is different, and the different proportion will cause some characteristics of zeolite changes, such as ion exchange and acid resistance.

The pore size of zeolite is uniform, the internal void structure is developed, the specific surface area is large, the adsorption capacity is strong, and contains a large number of invisible pore sizes. The pore size in 1g zeolite material can be expanded to the specific surface area of 500-1000m2, which is higher for special purposes. Good hydrophobicity The evaluation of the adsorption of zeolite depends not only on whether the specific surface area of zeolite is large enough, but also on whether the hydrophobicity of equipment is good. Activated Carbon Jiujiang When purchasing, people can choose the inspection equipment. When the air humidity for the hydrophobicity of the inspection equipment is greater than 60%, if the equipment is blocked and the machine works abnormally, people should carefully consider whether to purchase the equipment. It is important to know that the adsorption and hydrophobicity of the zeolite runner are equally important. 3、 High desorption efficiency The purification efficiency of zeolite is determined by absorption on the one hand and desorption function on the other, Activated Carbon high quality If the desorption efficiency of the equipment cannot meet the daily operation standard, the working efficiency of the zeolite runner will be affected if the time is long. Not only that, it will also affect the zeolite runner.

Activated Carbon Jiujiang Because the aluminum oxide tetrahedron of zeolite has a negative charge, and the skeleton hole contains cations, a strong electric field is formed around the cations. Therefore, the adsorption force of zeolite not only has a strong dispersion force, but also has a large electrostatic force. It is precisely because of this electrostatic relationship that zeolites have preferential selective adsorption on polar, unsaturated and polarizable molecules. It can strongly adsorb molecules containing polar groups such as hydroxyl ion, ammonium ion and other polarizable groups, especially water, which can form hydrogen bonds with aluminum silicon skeleton, so zeolite has strong water absorption. It can still adsorb even under low relative humidity and concentration, and its water absorption is higher than that of silica gel and activated alumina. The main material of honeycomb zeolite adsorbent is natural zeolite. The manufacturer of zeolite is composed of silica Inorganic microporous material composed of al_2o_3 and alkaline metal or alkaline earth metal, with inner pore volume accounting for 40-50% of the total volume and specific surface area of 100-500 m2/g, is characterized by high temperature resistance, non flammability, good thermal stability and hydrothermal stability. It is an efficient molecular sieve carrier with good adsorption performance, no secondary pollution, and can be regenerated at high temperature. Compared with honeycomb activated carbon, its performance is about 25% of its efficiency, However, it is widely used in the fields of adsorption, separation, catalysis and environment due to its high temperature resistance and difficult ignition. It is more suitable for the treatment of organic waste gas with large air volume and low concentration.