major Because the silicon (aluminum) oxygen tetrahedron of natural zeolite crystal has many holes and channels, which occupy cations and water molecules. When some other goods are completely dehydrated after baking, the crystal skeleton is not damaged, but forms large holes on the inner surface, which can absorb and store a large number of molecules, so it has the characteristics of large adsorption capacity and high selectivity. There are cavities and channels in the crystal structure of zeolite with large adsorption capacity, whose volume accounts for more than 50% of the total volume of zeolite crystals. Moreover, the micropores of zeolite are evenly distributed, and the pore size is small, which is equivalent to the molecular size of general substances. The internal surface area of zeolite crystals can reach more than 1000 square meters. Therefore, the adsorption capacity of zeolite is particularly large. manufactor In different zeolite minerals, the proportion of silicon and aluminum is different, and the different proportion will cause some characteristics of zeolite changes, such as ion exchange and acid resistance.

The main material of honeycomb zeolite molecular sieve is natural zeolite, which is an inorganic microporous material composed of SiO2, Al2O3 and alkaline metal or alkaline earth metal. Its inner pore volume accounts for 40-50% of the total volume, and its specific surface area is 300-1000 m2/g, which has the characteristics of high temperature resistance, non flammability, good thermal stability and hydrothermal stability, Yichun It is an efficient molecular sieve carrier with good adsorption performance, no secondary pollution, and can be regenerated at high temperature. Its efficiency is 40% higher than that of similar activated carbon. It is widely used in the fields of adsorption, separation, catalysis and environment, and is more suitable for the treatment of organic waste gas with large air volume and low concentration. major The adsorption material has a stable ozone decomposition ability, which significantly improves the decomposition efficiency of VOCs. The adsorption material first forms a special structural effect through the combination design of silver and manganese, which can decompose ozone into active oxygen atoms, and then react with VOCs molecules to form carbon dioxide and water.

Yichun Zeolite molecular sieve carrier has many advantages: 1. It is stable in operation, and the concentration of waste gas can reach the standard stably; 2. It can be desorbed at high temperature, with high regeneration efficiency and high safety; 3. Honeycomb zeolite is used as the adsorption carrier, with small resistance; 4. Compact structure, small floor area of the whole equipment. 5. It has a wide range of applications and is suitable for treating various organic waste gases. The main material of honeycomb zeolite adsorbent is natural zeolite. The manufacturer of zeolite is composed of silica Inorganic microporous material composed of al_2o_3 and alkaline metal or alkaline earth metal, with inner pore volume accounting for 40-50% of the total volume and specific surface area of 100-500 m2/g, is characterized by high temperature resistance, non flammability, good thermal stability and hydrothermal stability. It is an efficient molecular sieve carrier with good adsorption performance, no secondary pollution, and can be regenerated at high temperature. Compared with honeycomb activated carbon, its performance is about 25% of its efficiency, However, it is widely used in the fields of adsorption, separation, catalysis and environment due to its high temperature resistance and difficult ignition. It is more suitable for the treatment of organic waste gas with large air volume and low concentration. major

Zeolite molecular sieves have the following potential applications. manufactor (1) Due to the high whiteness of molecular sieves, the optical properties of paper can be improved. (2) It can improve the loose thickness and printability of the paper. (3) Molecular sieves can be used to prepare special papers such as gas filter paper, rust proof paper and photocatalysis paper due to their open structure. (4) It can be used for low weight newsprint and book paper, and can effectively avoid ink penetration. (5) Its ion exchange performance can avoid resin and filler deposition. major (6) It can be used for phenolic paper laminate to improve its corrosion resistance in humid environment. Phenolic paper laminates used as insulators in printed circuit boards and integrated circuits will be affected by electrolytic corrosion when exposed to high humidity. (7) It is mixed with titanium dioxide (TiO2) filler to produce high-quality white paper.

The main material of honeycomb zeolite adsorbent is natural zeolite. The zeolite manufacturer is an inorganic microporous material composed of sio2, al_2o_3 and alkaline metal or alkaline earth metal, major Its inner pore volume accounts for 40-50% of the total volume, and its specific surface area is 100-500 m2/g. It is characterized by high temperature resistance, non flammability, good thermal stability and hydrothermal stability. It is an efficient molecular sieve carrier with good adsorption performance, no secondary pollution, and can be regenerated at high temperature. Compared with honeycomb activated carbon, its performance is about 25% of its efficiency, but it has high temperature resistance and is not easy to ignite Catalysis and environment are widely used, which is more suitable for the treatment of organic waste gas with large air volume and low concentration. Zeolite adsorbent products include microporous adsorbent and mesoporous adsorbent. manufactor (1) Microporous molecular sieves with molecular pore size below 2 nm and mesoporous molecular sieves with molecular pore size between 2-50 nm (50 nm The above are macroporous molecular sieves), mesoporous molecular sieves have high specific surface area, regular and orderly pore structure, narrow pore size distribution, continuous and adjustable pore size and other characteristics, which make it play an important role in the adsorption, separation and catalytic reaction of macromolecules that are difficult for many microporous molecular sieves to complete. (2) Therefore, molecular sieve materials with different properties and pore sizes shall be configured according to the different components of organic waste gas during selection, so as to achieve targeted organic waste gas treatment, meet the design requirements and emission standards.

Molecular sieve has clear pore cavity distribution, extremely high internal surface area (600m2/s), good thermal stability (1000 ℃), and adjustable acid site center. The acidity of molecular sieve mainly comes from three coordinated aluminum atoms and aluminum ions (AlO)+on the framework and in the pores. OH based acid sensitive site center on molecular sieve HY obtained by ion exchange, Yichun The aluminum ions outside the framework will strengthen the acid site and form the L acid site center. Polyvalent cations such as Ca2+, Mg2+and La3+can show the acid site center after exchange. The reduction of transition metal ions such as Cu2+and Ag+can also form acid site centers. In general, the higher the Al/Si ratio, the higher the specific activity of OH group. The modification of zeolite acidity can introduce protons through direct exchange of dilute hydrochloric acid. This method often leads to dealumination of molecular sieve framework. So NaY will become NH4Y and then HY. Because there are uniform small internal pores in the molecular sieve structure, when the molecular linearity of reactants and products is close to the pore size of the crystal, the selectivity of the catalytic reaction often depends on the corresponding size of the molecule and pore size. major This selectivity is called shape selective catalysis. There are two mechanisms leading to shape selectivity. One is caused by the difference of diffusion coefficient of molecules participating in the reaction in the pore cavity, which is called mass transfer selectivity; The other is caused by the space limitation of the transition state of the catalytic reaction, which is called transition state selectivity.