The pore size of zeolite is uniform, the internal void structure is developed, the specific surface area is large, the adsorption capacity is strong, and contains a large number of invisible pore sizes. The pore size in 1g zeolite material can be expanded to the specific surface area of 500-1000m2, which is higher for special purposes. Good hydrophobicity The evaluation of the adsorption of zeolite depends not only on whether the specific surface area of zeolite is large enough, but also on whether the hydrophobicity of equipment is good. Honeycomb activated carbon Ji'an When purchasing, people can choose the inspection equipment. When the air humidity for the hydrophobicity of the inspection equipment is greater than 60%, if the equipment is blocked and the machine works abnormally, people should carefully consider whether to purchase the equipment. It is important to know that the adsorption and hydrophobicity of the zeolite runner are equally important. 3、 High desorption efficiency The purification efficiency of zeolite is determined by absorption on the one hand and desorption function on the other, Honeycomb activated carbon high quality If the desorption efficiency of the equipment cannot meet the daily operation standard, the working efficiency of the zeolite runner will be affected if the time is long. Not only that, it will also affect the zeolite runner.

Because there are uniform small internal pores in the molecular sieve structure, Honeycomb activated carbon Ji'an When the molecular linear degree of reactants and products is close to the pore size of the crystal, the selectivity of catalytic reaction often depends on the corresponding size of the molecule and pore size. This selectivity is called shape selective catalysis. There are two mechanisms leading to shape selectivity. One is caused by the difference of diffusion coefficient of molecules participating in the reaction in the pore cavity, which is called mass transfer selectivity; The other is caused by the space limitation of the transition state of the catalytic reaction, which is called transition state selectivity. Molecular sieve has clear pore cavity distribution, extremely high internal surface area (600m2/s), good thermal stability (1000 ℃), and adjustable acid site center. The acidity of molecular sieve mainly comes from three coordinated aluminum atoms and aluminum ions (AlO)+on the framework and in the pores. The OH based acid sensitive site center on the molecular sieve HY obtained by ion exchange, and the aluminum ion outside the framework will strengthen the acid site, forming the L acid site center. Polyvalent cations such as Ca2+, Mg2+and La3+can show the acid site center after exchange. The reduction of transition metal ions such as Cu2+and Ag+can also form acid site centers. In general, the higher the Al/Si ratio, the higher the specific activity of OH group. The modification of zeolite acidity can introduce protons through direct exchange of dilute hydrochloric acid. Honeycomb activated carbon high quality This method often leads to dealumination of molecular sieve framework. So NaY will become NH4Y and then HY.

The main material of honeycomb zeolite molecular sieve is natural zeolite, which is an inorganic microporous material composed of SiO2, Al2O3 and alkaline metal or alkaline earth metal. Its inner pore volume accounts for 40-50% of the total volume, and its specific surface area is 300-1000 m2/g, which has the characteristics of high temperature resistance, non flammability, good thermal stability and hydrothermal stability, Honeycomb activated carbon Ji'an It is an efficient molecular sieve carrier with good adsorption performance, no secondary pollution, and can be regenerated at high temperature. Its efficiency is 40% higher than that of similar activated carbon. It is widely used in the fields of adsorption, separation, catalysis and environment, and is more suitable for the treatment of organic waste gas with large air volume and low concentration. Honeycomb activated carbon high quality The adsorption material has a stable ozone decomposition ability, which significantly improves the decomposition efficiency of VOCs. The adsorption material first forms a special structural effect through the combination design of silver and manganese, which can decompose ozone into active oxygen atoms, and then react with VOCs molecules to form carbon dioxide and water.

Honeycomb activated carbon high quality Rely on its own unique void structure. The pore size of zeolite is uniform, the internal void structure is developed, the specific surface area is large, the adsorption capacity is strong, and contains a large number of invisible pore sizes. The pore size in 1g zeolite material can be expanded to the specific surface area of 500-1000m2, which is higher for special purposes. The mutual adsorption between molecules is also called "van der Waals gravity". Although molecular motion speed is affected by temperature, material and other factors, Honeycomb activated carbon production But it always keeps moving in the micro environment. Due to the mutual attraction force between molecules, when a molecule is trapped in the inner pore volume of zeolite, it will lead to more molecules being absorbed until the adsorption of zeolite is saturated.