Molecular sieve is a crystalline silicate or aluminosilicate, which is a pore and cavity system with molecular size (usually 0.3nm to 2.0nm) formed by connecting silicon oxygen tetrahedron or aluminum oxide tetrahedron through oxygen bridge bond, Activated Carbon Beijing Therefore, it has the characteristics of screening molecules. However, with the deepening of molecular sieve synthesis and application research, researchers have found phosphoaluminate molecular sieves, and the skeleton elements (silicon or aluminum or phosphorus) of molecular sieves can also be replaced by B, Ga, Fe, Cr, Ge, Ti, V, Mn, Co, Zn, Be and Cu, and the size of its pores and cavities can also reach more than 2 nm, Activated Carbon major Therefore, molecular sieves can be divided into silicon aluminum molecular sieves, phosphorus aluminum molecular sieves and skeleton heteroatom molecular sieves according to the composition of skeleton elements;
High honeycomb zeolite molecular sieve content The zeolite content of the zeolite runner is proportional to the adsorption concentration efficiency, Activated Carbon major Therefore, when choosing to purchase zeolite runner, the matching zeolite content should be selected in combination with the emission concentration of enterprise exhaust gas pollutants. 2、 With good hydrophobicity, choose to purchase zeolite with large specific surface area. 2) Select inspection equipment to test the hydrophobicity of equipment Activated Carbon Direct selling When the air humidity is greater than 60%, calibrate the equipment. If the equipment is blocked and the machine works abnormally, it indicates that the equipment has poor hydrophobicity, and you should carefully consider whether to purchase the equipment.
Activated Carbon Beijing Since the adsorption does not change chemically, Activated Carbon major As long as we try to drive away the molecules concentrated on the surface, zeolite molecular sieves will have adsorption capacity again. This process is the reverse process of adsorption, which is called the process of desorption or regeneration. Honeycomb zeolite molecular sieve is a kind of aluminosilicate material containing alkali metal or alkaline earth metal oxide with open framework and regular pore cage structure. It has been widely used since it was discovered by Swedish scientists in 1956, and then it has been widely used in petrochemical industry, environmental protection, bioengineering and other fields due to its special physical characteristics. And with the gradual expansion of the demand for zeolite molecular sieves, researchers began to expand a variety of synthetic methods of zeolite molecular sieves to meet the needs of various fields. Zeolite molecular sieve has super strong adsorption performance, which is due to a "surface force" generated by molecular gravity on the solid surface. When the fluid flows, some molecules in the fluid collide with the adsorbent surface due to irregular movement, resulting in molecular concentration on the surface, reducing the number of such molecules in the fluid to separation Purposes of clearing
The main material of honeycomb zeolite molecular sieve is natural zeolite, which is an inorganic microporous material composed of SiO2, Al2O3 and alkaline metal or alkaline earth metal. Its inner pore volume accounts for 40-50% of the total volume, and its specific surface area is 300-1000 m2/g, which has the characteristics of high temperature resistance, non flammability, good thermal stability and hydrothermal stability, Activated Carbon Beijing It is an efficient molecular sieve carrier with good adsorption performance, no secondary pollution, and can be regenerated at high temperature. Its efficiency is 40% higher than that of similar activated carbon. It is widely used in the fields of adsorption, separation, catalysis and environment, and is more suitable for the treatment of organic waste gas with large air volume and low concentration. Activated Carbon major The adsorption material has a stable ozone decomposition ability, which significantly improves the decomposition efficiency of VOCs. The adsorption material first forms a special structural effect through the combination design of silver and manganese, which can decompose ozone into active oxygen atoms, and then react with VOCs molecules to form carbon dioxide and water.
High silica zeolite type molecular sieves, this kind of zeolite has a series, and ZSM-5 is widely used, with ZSM-8 and ZSM-11 having the same structure; The other group is ZSM-21, ZSM-35 and ZSM-38. ZSM-5 is often called high silica zeolite, with the Si/Al ratio up to 50 and ZSM-8 up to 100. This group of molecular sieves also shows hydrophobic characteristics. Activated Carbon Direct selling Their structural units are similar to those of mordenite, consisting of pairs of five membered rings, with no cage like cavities and only channels. ZSM-5 has two sets of cross channels, one is straight through, the other is zigzag perpendicular to each other, both formed by ten yuan rings. The channel is oval and its window diameter is (0.55-0.60) nm. Activated Carbon major Zeolites belonging to the high silicon group also have silicalite-1 of all silicon type, which has the same structure as ZSM-5, and silicalite-2 is the same as ZSM-11.